BLS 598
PRODUCT DESCRIPTION
TYPICAL PROPERTIES OF UNCURED MATERIAL
Specific Gravity @ 25 °CLMSExtrusion Rate, g/min: | 1.27-1.32 |
Extrusion Rate, g/min:Pressure 0.62 MPa, time 15 seconds, temperature 25 °C:Semco Cartridge | 220-550 |
Flow, ISO 7390, mm:After 3 @ 25 °C | ≤13 |
Odor | No Acetic Odor |
TYPICAL CURING PERFORMANCE
Surface Cure
Tack Free Time, minutes:Cured @ 25 °C / 50±5 % RH | ≤25 |
TYPICAL PROPERTIES OF CURED MATERIAL
Cured for 7 days @ 25 °C / 50±5 % RH
Physical Properties | Tensile Strength, ISO 37 | N/mm2≥1.3 |
Elongation, ISO 37, % | ≥325 | |
Shore Hardness, ISO 868, DurometerA | 26-40 |
GENERAL INFORMATION
This product is not recommended for use in pure oxygenand/oroxygen rich systems and should not be selected asa sealant for chlorine orother strong oxidizing materials.For safe handling information on this product,consult the Safety Data Sheet (SDS).
Directions for use
1. For best performance bond surfaces should be clean andfreefrom grease.
2. Full performance properties will develop over 72 hours.
3. Moisture curing begins immediately after the productisexposed to the atmosphere, therefore parts to beassembled should be matedwithin a few minutes after theproduct is dispensed.
4. Excess material can be easily wiped away withnon-polarsolvents.
NOTE: BLSIN?598 is not recommended for useas a cylinder headgasket or head gasket sealant.
5. For full automatic applications a volumetricdispensingsystem is recommended.